Silicon Carbide (SiC) particles were synthesized by self-propagating high temperature synthesis (SHS) from a powder mixture of SiO2-C-Mg. The reaction was carried out in a SHS reactor under static argon gas at a pressure of 0.5 MPa. The standard Gibbs energy minimization method was used to calculate the equilibrium composition of the reacting species. The
effects of carbon mole ratio on the precursor mixture (C/SiO2/Mg: 1/1/2 to 3/1/2) and on the SiC conversion were investigated using X-ray diffraction and scanning electron microscope technique. The as-synthesized products of SiC-MgO powders were leached with 0.1M HCl acid solution to obtain the SiC particles.