Effects of Si69 treatment on fly ash particles and thermal ageing on the properties of NR/SBR blend
Narongrith Sombatsompop, Ekkachai Wimolmala, and Thirasuk Markpin
pp. 1377 - 1391
Abstract
The research involved property development of NR/SBR blend filled fly ash particles used for reinforcement in comparison with commercial silica. The effects of silica content and surface treatment by Si69 silane coupling agent were studied. The experimental results suggested that as the silica content from fly ash particles increased the cure time decreased. The increase in silica content in fly ash resulted in increases in tensile modulus, hardness, tears strength and percent compression set, but led to decreases in elongation at break, abrasion, percent resilience and tensile strength. When adding the silane coupling agent the cure time and overall mechanical properties were improved. After thermal ageing, the tensile modulus and tensile strength increased, but the elongation at break decreased. Overall results recommended that 20 phr of silica in 2% Si69-treated fly ash particles gave the optimum mechanical properties of the blend and can be used to replace the commercial silica.